Determination of electronic properties of nanostructures using reflection electron energy loss spectroscopy: Nano-metalized polymer as case study

Jamileh Deris, Shaaker Hajati, Sven Mosbæk Tougaard, Vladimir Zaporojtchenko

Research output: Contribution to journalJournal articleResearchpeer-review

27 Downloads (Pure)

Abstract

In this work, Au was deposited with nominal effective thickness of 0.8 nm on polystyrene (PS) at room temperature. According to previous study, using XPS peak shape analysis [S. Hajati, V. Zaporojtchenko, F. Faupel, S. Tougaard, Surf. Sci. 601 (2007) 3261-3267], Au nanoparticles (Au-NPs) of sizes 5.5 nm were formed corresponding to such effective thickness (0.8 nm). Then the sample was annealed to 200 °C, which is far above the glass transition of PS. At this temperature, the Au-NPs were diffused within the depth 0.5 nm-6.5 nm as found using nondestructive XPS peak shape analysis. Electrons with primary energy 500 eV were used because the electronic properties will then be probed in utmost surface (∼1 IMFP range of depths that is 1.8 nm for PS). By using QUEELS software, theoretical and experimental electron inelastic cross section, energy loss function, electron inelastic mean free path and surface excitation parameters were obtained for the sample. The information obtained here, does not rely on any previously known information on the sample. This means that the method, applied here, is suitable for the determination of the electronic properties of new and unknown composite nanostructures.

Original languageEnglish
JournalApplied Surface Science
Volume377
Pages (from-to)44-47
ISSN0169-4332
DOIs
Publication statusPublished - 2016

Keywords

  • Au nanoparticles
  • Electronic properties
  • Polystyrene
  • Reflection electron energy-loss spectroscopy

Fingerprint

Dive into the research topics of 'Determination of electronic properties of nanostructures using reflection electron energy loss spectroscopy: Nano-metalized polymer as case study'. Together they form a unique fingerprint.

Cite this