Experimental Approach for Mixed-mode Fatigue - Delamination Crack Growth with Large Scale Bridging in Polymer Composites

Liu Liu, John W. Holmes, Bent F. Sørensen, Søren Wahlgren

Publikation: Bidrag til tidsskriftTidsskriftartikelForskningpeer review

Abstrakt

An experimental apparatus utilizing double cantilever beam specimens loaded with uneven bending moments was developed to study the mixed-mode fatigue crack growth in composites. The approach is suitable when large-scale bridging of cracks is present. To illustrate the testing method, cyclic growth of delaminations in a typical fibre-reinforced polymer composite was investigated under a constant cyclic loading amplitude. Pure mode I, mode II and mixed-mode crack growth conditions were examined. The results, analysed using a J-integral approach, show that the double cantilever beam loaded with uneven bending moments configuration provides a robust approach to investigate the fatigue crack growth of composites for pure mode and mixed-mode cracking. A steady-state crack growth regime was observed for mode I and mixed-mode loading. For mode II loading, steady-state was absent, and a progressively decreasing crack growth rate observed. In addition to details concerning the equipment, a general discussion of the development of cyclic bridging laws for delamination growth in the presence of large-scale bridging is provided.

OriginalsprogEngelsk
TidsskriftJournal of Composite Materials
Vol/bind48
Udgave nummer25
Sider (fra-til)3111-3128
ISSN0021-9983
DOI
StatusUdgivet - 2014
Udgivet eksterntJa

Fingeraftryk Dyk ned i forskningsemnerne om 'Experimental Approach for Mixed-mode Fatigue - Delamination Crack Growth with Large Scale Bridging in Polymer Composites'. Sammen danner de et unikt fingeraftryk.

Citationsformater